Color Degradation of Napthol Jeans with TiO2-SiO2 Photocatalyst from Karangwuni Beach Sand, Kulon Progo

Shinta Amelia, Lukhi Mulia Shitopyta, Mila Utami W, Ida Sriyana

Abstract


The industries that produce the most liquid waste in Indonesia are the batik and textile industries. Napthol dyes are the most widely used dyes as dyes or batik dyes which are completely non-biodegradable and can cause cancer, digestive disorders, and weakening of the body's resistance due to disease and environmental pollution. One of the processing methods currently being developed to degrade color in liquid waste is the photocatalyst method. The photocatalyst method can use a photocatalyst semiconductor in the form of TiO2 with a supporting material in the form of SiO2. SiO2 as a supporting material can be obtained from the utilization of the local potential of Karangwuni Kulon Progo beach sand. Dye processing was carried out by varying the irradiation time and concentration of Naphtol Jeans. The degradation process was applied to a 25 ml sample solution with the addition of 5 gr/L catalyst for 24 hours, 48 hours, 72 hours, 96 hours, and 120 hours of irradiation. This study resulted in the highest reduction in naphtol concentration at the concentration variable of 100 ppm with a percentage of 44.4687% and a long irradiation time of 120 hours.


Keywords


Fotokatalis ; Naphtol Jeans ; Pasir Karangwuni ; TiO2 ; SiO2

References


Andari, N. D., & Wardhani, S. (2014). Fotokatalis TiO2-Zeolit untuk Degradasi Metilen Biru. Chem. Prog., 7(1), 9–14.

Dony, N., Azis, H., & Syukri. (2013). Studi Fotodegradasi biru metilen di Bawah Sinar Matahari oleh ZnO-SnO2 yang Dibuat dengan Metoda Solid State Reaction. Semirata FMIPA Universitas Lampung, 297–304.

Haedar, N., Fahruddin, Abdullah, A., Syam, N. A., & Talessang, N. H. (2019). Dekolorisasi dan Degradasi Limbah Zat Warna Naftol oleh Jamur dari Limbah Industri Batik. Ilmu Alam dan Lingkungan, 10(2), 1–8.

Hamu, G. V., Gauru, I., & Kadang, L. (2019). Pemanfaatan Arang Aktif Tempurung Kemiri (Aleurites moluccana L. Willd) Sebagai Adsorben Zat Warna Naphtol. Chem, Notes, 1(2), 12–23.

Irzon, R. (2018). Komposisi Kimia Pasir Pantai di Selatan Kulon Progo dan Implikasi terhadap Provenance. Jurnal Geologi dan Sumberdaya Mineral, 19(1), 31–45.

Ishmah, S. N. (2019). Ekstraksi Silika Pasir Pantai Bengkulu sebagai Fotokatalis dalam Remediasi Limbah. Skripsi.

Jannah, M. (2015). Pembuatan Silika Gel dari Abu Cangkang Kelapa Sawit dan Fiber Kelapa Sawit PT SPOI dengan Pengaruh Temperatur Ekstraksi. Skripsi. Palembang: Politeknik Negeri Sriwijaya.

Madina, F. E., Elvia, R., & Candra, I. N. (2017). Analisis Kapasitas Adsorpsi Silika Dari Pasir Pantai Panjang Bengkulu Terhadap Pewarna

Rhodamine B. Jurnal Pendidikan dan Ilmu Kimia, 1(2), 98–101.

Miller, J. N., & Miller, J. C. (2010). Statistics and Chemometries for Analytical Chemistry Sixth Edition. England: Pearson Education.

Munasir, Triwikantoro, Zainuri, M., & Darminto. (2013). Ekstraksi dan Sintesis Nanosilika Berbasis Pasir Bancar dengan Metode Basah. Jurnal Penelitian Fisika dan Aplikasinya (JPFA), 3(2), 12–17.

Naimah, S., & Ermawati, R. (2011). Efek Fotokatalisis Nano TiO2 Terhadap Mekanisme Antimikrobia E Coli dan Salmonella. Indonesian Journal of Industrial Research, 5(2), 113–120.

Nurillahi, R., Halimah, D. N., Apriliani, D. G., & Fatimah, I. (2020). Pengolahan Limbah Batik Cair menggunakan Fotokatalis TiO2-Abu Vulkanik Desa Wukirsari Yogyakarta. Khazanah:Jurnal Mahasiswa, 10(2), 1–8.

Pataya, S. A., Gareso, P. L., & Juarlin, E. (2016). Karakterisasi Lapisan Tipis Titanium Dioksida (TiO2) yang Ditumbuhkan dengan Metode Spin Coating Diatas Substrat Kaca. Jurnal Kimia, 1–8.

Perdana, N. D., Wardhani, S., & Khunur, M. M. (2014). Pengaruh Penambahan Hidrogen Peroksida (H2O2) Terhadap Degradasi Methylene Blue dengan Menggunakan Fotokatalis ZnO-Zeolit.. Kimia Student Journal, 2(2), 576–582.

Permatasari, O. S., Wardhani, S., & Darjito. (2015). Studi Pengaruh Penambahan H2O2 Terhadap Degradasi Methyl Orange Menggunakan Fotokatalis TiO2-N. Kimia Student Journal, 1(1), 661–667.

Prastiwi, W. D., Maulana, K. D., Wibowo, E. A. P., Aji, N. R., & Setyani,

A. (2017). Sintesis dan Karakteristik TiO2 dan SiO2 Serta Aplikasinya Terhadap Kadar Fe Dalam Air Sumur. Jurnal Ilmiah Sains, 17(1), 30–34.

Pristantho, J. F. (2011). Degradasi Fotokatalitik Surfaktan NaLS (Natrium Lauril Sulfat) dengan Kombinasi Reagen Fenton dan TiO2. Doctoral Dissertation. Universitas Airlangga.

Qodri, A. A. (2011). Fotodegradasi Zat Warna Remazol Yellow FG dengan Fotokatalis Komposit TiO2 /SiO2. Skripsi. Kimia, FMIPA, UNS.

Rakhmawati, D., Jati, A. W. N., & Yulianti, L. I. M. (2012). Remediasi Limbah Proses Pewarna Naphtol. Unpublished undergraduate thesis, Universitas Atma Jaya:Yogyakarta.

Retnosari, A. (2013). Ekstraksi dan Penentuan Kadar Silika (SiO2) Hasil Ekstraksi dari Abu Terbang (Fly Ash) Batubara. Skripsi. Kimia, FMIPA, Universitas Jember.

Saraswati, I. G. A. A., Diantariani, N. P., & Suarya, P. (2015). Fotodegradasi Zat Warna Tekstil Congo Red dengan Fotokatalis ZnO-Arang Aktif dan Sinar Ultraviolet (UV). JURNAL KIMIA, 9(2), 175–182.

Sitanggang, P. Y. (2017). Pengolahan Limbah Tekstil dan Batik Di Indonesia. Departemen Teknik Kimia Institut Teknologi Bandung, Bandung, 1, 2–3.

Sumarno, T, P. N., Januarty, M., & Yuniarti, Y. (2015). Pemurnian Pasir Silika dengan Metode Leaching Asam dan Bantuan Sonikasi. Proceeding Seminar Nasional Kejuangan, 1–8.

Suprihatin, H. (2014). Kandungan Organik Limbah Cair Industri Batik Jetis Sidoarjo dan Alternatif Pengolahannya. Pusat Penelitian Lingkungan Hidup Universitas Riau, 130–138.

Wahdah, R. (2013). Kadar Amonia (NH3) Pada Urin Bayi Laki-Laki dan Bayi Perempuan yang Berusia Kurang Dari Enam Bulan dan Kaitannya dengan Perbedaan Hukum Kenajisannya Menurut Islam. Skripsi. IAIN Walisongo.

Wijayanto, A. T. (2013). Fotodegradasi Metilen Biru Menggunakan Komposit TiO2-SiO2. Skripsi. Kimia, Fakultas Sains dan Teknologi, UIN Sunan Kalijaga.

Yoga, I. K. W. (2015). Penentuan Konsentrasi Optimum Kurva Standar

Antioksidan ; Asam Galat , Asam Askorbat dan Trolox® Terhadap Radikal Bebas DPPH (2,2-diphenyl-1-picrylhydrazyl ) 0,1 mM. Proceedings Seminar Nasional FMIPA UNDIKSHA V, 316–321.




DOI: https://doi.org/10.31315/e.v20i1.8990

Refbacks

  • There are currently no refbacks.

Article Metrics

Metrics Loading ...

Metrics powered by PLOS ALM


Eksergi p-ISSN  1410-394X, e-ISSN 2460-8203,  is published by "Prodi Teknik Kimia UPN Veteran Yogyakarta".

Contact  Jl. SWK 104 (Lingkar Utara) Condong catur Sleman Yogyakarta

 

 Creative Commons License

Eksergi by http://jurnal.upnyk.ac.id/index.php/eksergi/index/ is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.

 

 

Lihat Statistik Jurnal Kami